| Nickel bis(sulphamidate) Chemical Properties |
| Provider |
Language |
| ALFA |
English |
| |
| Nickel bis(sulphamidate) Usage And Synthesis |
| Electroplating main salt |
Nickel sulfamate is an excellent electroplating main salt, is dark green transparent liquid, at high temperature or low pH is susceptible to hydrolysis. Soluble in water, liquid ammonia, ethanol, slightly soluble in , aqueous solution is acidic, hygroscopic, in moist air deliquescence quickly. In dry air slowly weathering, will lose four molecules of water upon heating, begins to decompose and form base salts at temperatures above 110℃, continued to heat and generate the mixture of brown-black nickel oxide and green nickel oxide. Because of its coating with low internal stress, fast plating speed, high solubility, no pollution, becomes one kind of rapidly developed electroplating main salt on the international in recent years, has been widely used in industries such as precision electroplating, electronics, printed circuit board plating, automotive, aerospace, weapons, coinage, metallurgy, nickel screen, radio, nickel-plated, colored metal, nickel catalysts, ceramics brown pigment, and color aluminum alloy. Nickel sulfamate provides the desired nickel metal ion for nickel plating and plays the role as a conductive salt, nickel salt content is high, can use a higher cathode current density, deposition speed is fast, commonly used for high-speed thick nickel-plated. But the too high concentration will reduce the polarization of cathode, poor dispersion ability, and plating solution with a large loss. Low nickel salt content has low deposition rate, but good dispersing ability, can obtain fine crystal and bright coating. But stability of Nickel sulfamate is poor, the cost is relatively high. |
| sulfamic acid |
sulfamic acid is a sulfuric acid derivative, has an amino functional group and a sulfonic acid functional group, can be performed chemical reaction with a variety of substances, an aqueous solution has equivalent of a strong acidity of hydrochloric acid and sulfuric acid, also known as a solid sulfuric acid, having characteristics of non-volatile, not absorb moisture, no odor and minimal human toxicity. But the skin cannot be contact with an amino acid for long time, even more cannot enter the eye. When at the ambient temperature is very stable and can be maintained unchanged for several years; when the temperature reaches 209 ℃, begins to decompose. Soluble in water and liquid ammonia, slightly soluble in methanol, insoluble in alcohol, r, hydrocarbons and carbon disulfide. Although its solution is strongly acidic, but corrosivity to metal is small than mineral acid, the effect on iron corrosion products is slow, can add some sodium chloride, to make it slow to produce hydrochloric acid, which can effectively dissolve iron dirty. Also can remove scale and corrosion products of the surface of the devices such as iron, steel, copper and stainless steel. It is the only useful as cleaning acid for galvanized metal surface. When the use of sulfamic acid aqueous solution to clean, the temperature is controlled not to exceed 66 ℃ (to prevent decomposition of sulfamic acid), concentration does not exceed 10%.
The above information is edited by the chemicalbook of Liu Yujie. |
|
|
|
|
|